AWS E309MoL Stainless steels Manual electrode weld fabrication data
Application&Standard&Note:
1. Suitable FOR STAINLESS STEEL AND CARBON STEEL OR LOW ALLOY steel DISsimilar STEEL WELDING, STAINLESS steel composite plate cladding WELDING, 316 SERIES STAINLESS STEEL SURFACING WELDING on carbon steel or low alloy STEEL.
2. The standard we met: GB/T983 E309LMo-16, AWS A5.4 E309LMo-16 & A5.4M E309LMo-16, ISO3581-A:E(23 12 2 L) R 1 2, ISO3581-B:ES309LMo-16
Welding process control:
Low voltage arc welding; The electrode swing can not be too wide, generally within 3 times the diameter of the electrode; Welding speed can not be too slow, in case of overheating and slag, but in case of easy cracking, choose low current slow welding. Vertical welding due to the characteristics of stainless steel water is easy to flow, the best choice is to use broken arc welding. Multi - layer welding must be cleaned up welding slag. The arc pit must be filled when the arc is closed.
Features
1. Titanium calcium stainless steel electrode, the main composition is 22% CR-12%Ni-2%Mo
2. Stable arc, beautiful forming, fine ripples, few splashes, easy de-slagging, good fire resistance of drug skin, good stomatal resistance.
3. The weld metal contains more ferrite,due to add Mo, it has low crack sensitivity.
Titanium calcium type of ultra-low carbon Cr23Ni13Mo2Cu stainless steel electrode, AC and DC dual use, the weld with the right amount of molybdenum, improve the weld metal crack resistance and corrosion resistance. Used for the same type of ultra-low carbon stainless steel and dissimilar steel.
Company & Factory
Product composition and mechanical properties introduction
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RULES | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
AWS RULES | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
EXAMPLE VALUE | 0.028 | 1.43 | 0.77 | 23.2 | 13.1 | 2.5 | 0.027 | 0.006 | 0.1 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | HEATTREAMENT℃xh | IMAPACT VALUE J/℃ | ELONGATION(%) | |||||||||
GB/T RULES | - | 510 | - | - | 25 | |||||||||
AWS RULES | - | 520 | - | - | 30 | |||||||||
EXAMPLE VALUE | - | 660 | - | - | 34 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||||
ELECTRICITY (Amp) |
H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
PACKING DETAILES:
SEPCIFICATION | LENGTH | PCS/1KG | WEIGHT/1KG | |||
2.0mm | 300mm | 79PCS | 2KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27PCS | 5KG | |||
4.0mm | 350mm | 16PCS | 5KG | |||
5.0mm | 350mm | 12PCS | 5KG |
NOTE:
H/W: horizontal position welding
O/W: over-head position welding
Typical Cases
Certificate
Product composition and mechanical properties introduction
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RULES | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
AWS RULES | 0.04 | 0.5-2.5 | 1.00 | 22.0-25.0 | 12.0-14.0 | 2.0-3.0 | 0.040 | 0.03 | 0.75 |
EXAMPLE VALUE | 0.028 | 1.43 | 0.77 | 23.2 | 13.1 | 2.5 | 0.027 | 0.006 | 0.1 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | HEATTREAMENT℃xh | IMAPACT VALUE J/℃ | ELONGATION(%) | |||||||||
GB/T RULES | - | 510 | - | - | 25 | |||||||||
AWS RULES | - | 520 | - | - | 30 | |||||||||
EXAMPLE VALUE | - | 660 | - | - | 34 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||||
ELECTRICITY (Amp) |
H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
PACKING DETAILES:
SEPCIFICATION | LENGTH | PCS/1KG | WEIGHT/1KG | |||
2.0mm | 300mm | 79PCS | 2KG | |||
2.6mm | 300mm | 48PCS | 2KG | |||
3.2mm | 350mm | 27PCS | 5KG | |||
4.0mm | 350mm | 16PCS | 5KG | |||
5.0mm | 350mm | 12PCS | 5KG |
NOTE:
H/W: horizontal position welding
O/W: over-head position welding