China wholesale Carbon Steels E8015-G Weld Fabrication Makings Manufacturer - 490Mpa Hand Electrode For High Strength Steel – Honest Metal

Application&Standard

1.Suitable FOR WELDING OF CARBON STEEL AND LOW ALLOY STEEL, AS WELL AS THE corresponding strength of boiler, pipeline, pressure vessel, ocean engineering structure welding, such as Q345, X60 pipeline steel, etc.
2. The standard we met: GB/T5117 E5015-G AP, AWS A5.5 E7015-G & A5.5M E4915-G, ISO2560-A:E 42 4 Z0.5 Ni B 2 2, ISO 2560-B: E4915 G-AP

Points for attention:

1. Before welding, the electrode must be baked at 350℃ for 1 hour and taken as needed.
2. Before welding, the weldment must be cleaned of rust, oil, water and other impurities.
3. Welding must be performed with short arc, narrow pass welding is appropriate.

Features

1. Low hydrogen potassium electrode, stable arc, beautiful forming, exquisite, little splash, easy de-slagging, good skin fire resistance, good porosity resistance.
2. table mechanical properties, good plasticity, impact toughness and crack resistance.Diffused hydrogen content is low.

J507RH conforms to GBE5015-G. Tensile strength 500~600MPa yield strength 420~450MPa impact to 40 degrees can reach 100~120JRH is ultra-low hydrogen high toughness electrode. 1. The front electrode shall be baked at 350-430℃ for 1h, and then placed in the incubator at 100-150℃ for use with baking. 2. Before welding, the weldment shall be cleaned of rust, oil, water and other impurities. 3. Short arc should be used during welding, and narrow weld passage is appropriate.

Company & Factory

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

MECHANICAL PROPERTY:

RECOMMENDED WELDING PARAMETERS:

NOTE:
H/W: horizontal position welding
O/W: over-head position welding

Typical Cases

Certificate