We have now our possess revenue group, design staff, technical crew, QC team and package group. We now have strict excellent regulate procedures for each process. Also, all of our workers are experienced in printing subject for Hard-Facing Flux Cored Wire Welding Makings, Nickel Alloys Weld Fabrication, Hard-Facing Flux Cored Wire Metal Jointing, Honesty is our principle, skilled procedure is our perform, service is our target, and customers' satisfaction is our long term!

China wholesale Hard-Facing Metal Jointing Makings Factory - AWS A5.13 ENiCrFe-1 Nickel alloys Manual electrode Welding accessories – Honest Metal Detail:

Application & Standard

This COBALT-BASED SURFACING ELECTRODE CAN BE USED FOR LINING SLEEVE OF SHAFT SLEEVE, CUTTING EDGE OF CHEMICAL FIBER EQUIPMENT, SAWTOOTH, SCREW PUSH ROD, HIGH temperature and HIGH pressure VALVE AND HIGH pressure pump ETC. The surface roughness of the workpiece should be less than Ra12.5μm, and the surface rust, oil and other dirt should be strictly removed. The matrix should not have cracks, pores, sand and other defects, and the edges and corners should be rounded. Before surfacing, different temperatures should be selected according to the substrate material for preheating. When the matrix material is pearlitic heat-resistant steel or martensitic stainless steel and other materials with poor welding performance, the austenitic stainless steel surfacing layer should be welded on the matrix surface, and then the cobalt-based alloy should be surfacing after smooth processing to improve the crack resistance and avoid cracks. Either AC or DC arc welding power supply can be used for D802 and D812 electrodes. Dc arc welding power supply is recommended.

Features

GEH-SL12 titanium calcium coated cobalt-base surfacing electrode. Cobalt-cr-tungsten alloy is used as the core wire. Dc reverse connection is recommended. Surfacing metal can maintain good wear resistance and corrosion resistance at 650℃. Before welding, it must be baked at 300-350℃ for 1 hour; The hardening layer on the base metal surface should be removed to avoid cracks and brittleness. According to the size of the base metal workpiece and the type of base metal, it must be preheated at 300-600℃, and small current short arc welding is appropriate.

High Carbon steels Solid wire welding accessories
未标题-2

Company & Factory

factory2

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Ni	P	Fe	Nb+Ta	S
GB/T RULES	0.08	3.5	0.80	13.0-17.0	≥62	0.02	11.0	0.5-4.0	0.015
AWS RULES	0.08	3.5	0.75	13.0-17.0	≥	0.03	11.0	1.5-4.0	0.015
EXAMPLE VALUE	0.048	2.97	0.34	15.6	69.6	0.005	8.94	2.65	0.007

RECOMMENDED WELDING PARAMETERS:

DIAMETERS SPECIFICATIONS(mm)		2.6*300	3.2*350	4.0*350
ELECTRICITY (Amp)	Flat/horizontal welding	69-95	70-115	95-145
	Vertical/overhead welding	55-80	65-110	80-130

asgvsbsb

TYPICAL CASES

430Mpa Hand Electrode For Low Carbon Steel05
典型项目

Certificates

certificate

Product detail pictures:

Related Product Guide:

With our loaded working experience and thoughtful products and services, we've got been acknowledged as a reputable supplier for most international buyers for China wholesale Hard-Facing Metal Jointing Makings Factory - AWS A5.13 ENiCrFe-1 Nickel alloys Manual electrode Welding accessories – Honest Metal , The product will supply to all over the world, such as: Panama, Belgium, Portugal, We have got constantly insisted on the evolution of solutions, spent good funds and human resource in technological upgrading, and facilitate production improvement, meeting the wants of prospects from all countries and regions.

Hard-Facing Flux Cored Wire Metal Stuff