With a complete scientific quality management system, good quality and good faith, we win good reputation and occupied this field for Double Fillet Weld, Stainless Steels Seal Connection, Hard-Facing Flux Cored Wire Welding Makings, We can customize the products according to your requirements and we can pack it for you when you order.

China wholesale Soldering Rod Material Factory - AWS E7018-A1 Low-alloy steels Metal powder welding wire Welding accessories – Honest Metal Detail:

Application&Standard&Note：

AWS E7018-A1 (R106Fe) heat-resistant steel hand electrode is suitable for welding boiler pipe, heat exchanger heating surface pipe and steam pipe below 450℃ (such as 15MoG, T1, P1 steel) and other occasions. Such as ASTM A204 and A335-P1 tubes; The weldment should be preheated to 90-110℃ before welding, and maintain the interlayer temperature. Can also be used for welding general low alloy steel high strength steel structure. And this hand electrode can be used for full position welding. According to the characteristics of the production process of low-temperature liquefied gas, the low-temperature steel is used in different grades according to different service temperatures (-40℃, -70℃, -100℃, -194℃, -253℃), and the corresponding welding materials are selected.

Features

This kind of hand electrode is iron powder low hydrogen type hand electrode, adding iron powder, high melting efficiency; 0.5% Mo is added to improve weld strength and corrosion resistance; And the arc is stable, less splashing, forming, desagging is easy, X-Ray performance is good.

The common alloying elements of pearlitic heat resistant steel are chromium, molybdenum, vanadium, niobium and so on to meet different working requirements. Due to the joint action of carbon alloy elements in steel, it is easy to form hardened structure during welding, and the welding performance is poor. Therefore, pearlitic heat-resistant steel is generally preheated before welding and tempered after welding.

High Carbon steels Solid wire welding accessories
High Carbon steels Manual electrode welding accessories

Company & Factory

factory2

Product composition and mechanical properties introduction

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Mo	P	S
GB/T RULES	0.12	1.00	0.80	-	0.40-0.65	0.03	0.030
AWS RULES	0.12	0.90	0.80	-	0.40-0.65	0.03	0.030
EXAMPLE VALUE	0.6	0.7	0.31	0.035	0.5	0.012	0.01

MECHANICAL PROPERTY:

PROPERTY	YIELD STRENGTH(MPa)	EXTENSION STRENGTH(MPa)	HEATTREAMENT℃xh	IMAPACT VALUE J/℃	ELONGATION(%)
GB/T RULES	390	490	620*1	-	22
AWS RULES	390	490	620*1	-	22
EXAMPLE VALUE	480	570	620*1	170/Normal temperature	26

RECOMMENDED WELDING PARAMETERS:

DIAMETERS SPECIFICATIONS(mm)		2.6*350	3.2*350	4.0*400	5.0*400
ELECTRICITY (Amp)	H/W	80-110	100-130	130-180	170-210
	O/W	60-100	80-120	120-160	-

PACKING DETAILES：

SEPCIFICATION	LENGTH	PCS/1KG	WEIGHT/1KG
2.6mm	300mm	48PCS	2KG
3.2mm	350mm	27PCS	5KG
4.0mm	350mm	16PCS	5KG
5.0mm	350mm	12PCS	5KG

430Mpa Hand Electrode For Low Carbon Steel04

Typical Cases

430Mpa Hand Electrode For Low Carbon Steel05
典型项目

Certificate

certificate

Product detail pictures:

Related Product Guide:

Every single member from our higher effectiveness product sales staff values customers' requires and organization communication for China wholesale Soldering Rod Material Factory - AWS E7018-A1 Low-alloy steels Metal powder welding wire Welding accessories – Honest Metal , The product will supply to all over the world, such as: Bulgaria, Curacao, Milan, To get more information about us as well as see all our products, please visit our website. To get more information please feel free to let us know. Thank you very much and wish your business always be great!

Flux Material In Soldering