Hard-facing SAW welding wire and welding flux weld fabrication accessories

GEH-507 is a hand electrode in line with GB/T984 EDCr-A1-15 applied to valves and other seals. It mainly ADAPTS to the working environment temperature below 450℃. In the market, the application of this product is very wide and popular. Can use DC reverse surfacing high chromium steel, surfacing metal for 1Cr13, chromium martensitic steel. Under our strict control of product quality and production technology, the delivery pass rate of this product is very high. We produce 3.2mm,4.0mm,5.0mm hard surface wear-resistant hand electrodes for customers, and support product customization.


  • Brand:: Gintune
  • Item No:: GEH-507
  • Suit for:: Valve hardfacing
  • Power supply polarity:: DC+
  • Certificate authority:: NONE
  • Welding position: Hard-facing  SAW welding wire and  welding flux weld fabrication accessories
  • Product Detail

    Sepcification

    Product Tags

    Application & Standard

    This product is mainly used for surfacing the valves and other sealing parts of high-rise boiler units in power stations working at 570℃ or below. Adopt DC reverse connection. The surfacing metal is 1Cr13 semi-ferritic high chromium steel. Generally no heat treatment is required during welding, and the hardness is uniform. It can be annealed and softened at 750-800℃. When heated to 900-1000℃, it can be re-hardened by air cooling or oil quenching. This hand electrode is also used for surfacing of shaft and valve of carbon steel or alloy steel at working temperature below 450℃. The hardness of the surfacing layer should be controlled at about 40.

    Features

    GEH-507 is China GB/T984EDCr-A1-15 under a low sodium hydrogen type high chromium steel for valve surfacing welding electrode, good operation, less splash, easy slag removal, beautiful shape, can be easily mechanical processing. And the surfacing layer has the characteristics of air quenching, high medium-temperature hardness and good corrosion resistance. This TYPE OF ELECTRODE IS often USED FOR metal wear and moisture, weak acid and other action of parts, such as valve sealing surface, mixer slurry, etc. Before welding, it must be dried at 300-350℃ for 1 hour. To remove the base material surface moisture, rust stains, oil. And we should pay attention to the way of arc and arc. After the arc will arc back burning, remelting arc point, when the arc to fill the arc pit.

    High Carbon steels Solid wire welding accessories
    未标题-2

    Company & Factory

    factory2

    Product composition and mechanical properties introduction

    CHEMICAL COMPONET:

    ALLOY(wt%) C Mn Si Cr P S
    GB/T RULES 0.15 - - 10.00-16.00 0.04 0.03
    AWS RULES - - - - - -
    EXAMPLE VALUE 0.12 0.60 1.00 12.8 0.025 0.008

    RECOMMENDED WELDING PARAMETERS:

    DIAMETERS SPECIFICATIONS(mm) 3.2*350 4.0*350 5.0*350
    ELECTRICITY
    (Amp)
    80-120 120-160 160-210
    asgvsbsb

    TYPICAL CASES

    430Mpa Hand Electrode For Low Carbon Steel05
    典型项目

    Certificates

    certificate

    Product composition and mechanical properties introduction

    CHEMICAL COMPONET:

    ALLOY(wt%) C Mn Si Cr P S
    GB/T RULES 0.15 - - 10.00-16.00 0.04 0.03
    AWS RULES - - - - - -
    EXAMPLE VALUE 0.12 0.60 1.00 12.8 0.025 0.008

    RECOMMENDED WELDING PARAMETERS:

    DIAMETERS SPECIFICATIONS(mm) 3.2*350 4.0*350 5.0*350
    ELECTRICITY
    (Amp)
    80-120 120-160 160-210