Hard-facing SAW welding wire and welding flux weld fabrication stuff

GEH-90 is a hard surface wear-resistant hand electrode in accordance with GB/T984 EDPCrMo-A5-15 standard, suitable for surfacing or repair welding of various metal surfaces. It is widely used in the market. In addition, under the advanced production technology, strict source control and quality inspection standards, our products have won a good reputation in the market and created a large number of sales. It has achieved quite high customer evaluation.


  • Brand:: Gintune
  • Item No:: GEH-90
  • Suit for:: Valve hardfacing
  • Power supply polarity:: DC+
  • Certificate authority:: NONE
  • Welding position: Hard-facing  SAW welding wire and  welding flux weld fabrication stuff
  • Product Detail

    Sepcification

    Product Tags

    Application & Standard

    This hard surface WEAR-resistant hand electrode is mainly suitable for low impact, intense wear parts, such as civil construction machinery surfacing regeneration, especially dredging machinery, bucket, sand suction pump. Surfacing is a welding method in which the surface or edge of steel parts is fused with a layer of wear resistance, corrosion resistance, high temperature resistance and other characteristics of metal materials. To repair and improve the service life of parts, effective use of raw materials, improve product performance, cost control has obvious economic benefits. The standard of surfacing is very complex. It is necessary to adopt suitable welding wire according to different rules. Different surfacing processes should be used for different steel parts and surfacing electrodes to obtain satisfactory actual surfacing results.

    Features

    This is a low sodium hydrogen coating type surfacing electrode, high hardness, no need of heat treatment, can not continue cutting, good wear resistance. Wear - resistant correct operation process can ensure that all the skin can be melted into the molten pool through the arc during fusion welding. And weld core, substrate surface metal rapidly melting to produce a new wear-resistant alloy. At the same time, efforts should be made to improve the carbon content of the electrode on the premise of ensuring that the welding layer has excellent crack resistance. Promote the formation of various carbides, increase its wear resistance. For the parts that bear impact and abrasive wear at the same time in the work, such as the hammer head of the crusher, lining plate, cage rod, etc. The above welding layer is far from meeting the requirements of its working conditions, and a completely different operation process must be adopted.

    High Carbon steels Solid wire welding accessories
    未标题-2

    Company & Factory

    factory2

    Product composition and mechanical properties introduction

    CHEMICAL COMPONET:

    ALLOY(wt%) C Mn Si Cr P S
    GB/T RULES 0.50-0.80 0.50-1.50 1.00 4.00-8.00 0.035 0.035
    AWS RULES - - - - - -
    EXAMPLE VALUE 0.64 1.35 0.94 7 0.027 0.007

    RECOMMENDED WELDING PARAMETERS:

    DIAMETERS SPECIFICATIONS(mm) 3.2*350 4.0*350 5.0*350
    ELECTRICITY
    (Amp)
    80-120 120-160 160-210
    asgvsbsb

    TYPICAL CASES

    430Mpa Hand Electrode For Low Carbon Steel05
    典型项目

    Certificates

    certificate

    Product composition and mechanical properties introduction

    CHEMICAL COMPONET:

    ALLOY(wt%) C Mn Si Cr P S
    GB/T RULES 0.50-0.80 0.50-1.50 1.00 4.00-8.00 0.035 0.035
    AWS RULES - - - - - -
    EXAMPLE VALUE 0.64 1.35 0.94 7 0.027 0.007

    RECOMMENDED WELDING PARAMETERS:

    DIAMETERS SPECIFICATIONS(mm) 3.2*350 4.0*350 5.0*350
    ELECTRICITY
    (Amp)
    80-120 120-160 160-210