Low-alloy steels Flux cored wire E81T1-B2C Welding stuff
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | V | Mo | P | S |
GB/T RULES | 0.05-0.12 | 1.25 | 0.80 | 1.00-1.50 | - | 0.40-0.65 | 0.03 | 0.03 |
AWS RULES | 0.05-0.12 | 1.25 | 0.80 | 1.00-1.50 | - | 0.40-0.65 | 0.03 | 0.03 |
EXAMPLE VALUE | 0.052 | 0.88 | 0.28 | 1.12 | 0.105 | 0.46 | 0.009 | 0.005 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Heat treatment°Cxh | |||||
GB/T RULES | 470 | 550-690 | - | 17 | 730*2 | |||||
AWS RULES | 470 | 550-690 | - | 19 | 730*2 | |||||
EXAMPLE VALUE | 560 | 640 | 50/Normal temperature | 23 | 730*2 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | ||||
Volt | 24-35 | ||||
Amp | 160-320 | ||||
Dry extension length(mm) | 15-20 | ||||
Gas flow(l/min) | 15-25 |
The arc is soft and stable, less splash, beautiful forming.
Good slag removal, less soot.
With excellent welding process performance.
-
Zhenhai Refining 1 million tons/year ethylene project
-
Welding materials for rail cars
-
JU2000E jack-up drilling rig
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | V | Mo | P | S |
GB/T RULES | 0.05-0.12 | 1.25 | 0.80 | 1.00-1.50 | - | 0.40-0.65 | 0.03 | 0.03 |
AWS RULES | 0.05-0.12 | 1.25 | 0.80 | 1.00-1.50 | - | 0.40-0.65 | 0.03 | 0.03 |
EXAMPLE VALUE | 0.052 | 0.88 | 0.28 | 1.12 | 0.105 | 0.46 | 0.009 | 0.005 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Heat treatment°Cxh | |||||
GB/T RULES | 470 | 550-690 | - | 17 | 730*2 | |||||
AWS RULES | 470 | 550-690 | - | 19 | 730*2 | |||||
EXAMPLE VALUE | 560 | 640 | 50/Normal temperature | 23 | 730*2 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | ||||
Volt | 24-35 | ||||
Amp | 160-320 | ||||
Dry extension length(mm) | 15-20 | ||||
Gas flow(l/min) | 15-25 |