Low-alloy steels Manual electrode E8018-C2 Soldering data
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Ni | Cr | Mo | P | S |
GB/T RULES | 0.12 | 1.25 | 0.80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
AWS RULES | 0.12 | 1.25 | 0.80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
EXAMPLE VALUE | 0.045 | 0.75 | 0.22 | 3.52 | 0.04 | 0.06 | 0.007 | 0.004 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Heat treatment°Cxh | |||||
GB/T RULES | 460 | 550 | 27/-75 | 17 | 605*1 | |||||
AWS RULES | 460 | 550 | 27/-75 | 19 | 605*1 | |||||
EXAMPLE VALUE | 495 | 600 | 100/-75 | 26 | 605*1 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||
ELECTRICITY (Amp) |
H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |
Iron powder low hydrogen type hand electrode.
Due to the addition of iron powder, the melting efficiency is higher, the impact toughness of the molten metal at -75℃.
Stable arc, less splash, good forming, easy slag removal, X-Ray performance is excellent.
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Ni | Cr | Mo | P | S |
GB/T RULES | 0.12 | 1.25 | 0.80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
AWS RULES | 0.12 | 1.25 | 0.80 | 3.00-3.75 | - | - | 0.03 | 0.03 |
EXAMPLE VALUE | 0.045 | 0.75 | 0.22 | 3.52 | 0.04 | 0.06 | 0.007 | 0.004 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Heat treatment°Cxh | |||||
GB/T RULES | 460 | 550 | 27/-75 | 17 | 605*1 | |||||
AWS RULES | 460 | 550 | 27/-75 | 19 | 605*1 | |||||
EXAMPLE VALUE | 495 | 600 | 100/-75 | 26 | 605*1 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | ||||
ELECTRICITY (Amp) |
H/W | 80-110 | 100-130 | 130-180 | 170-210 | |||
O/W | 60-100 | 80-120 | 120-160 | - |