Stainless Steels Flux Cored Wire E308LT1-4 jack-up rigs Consumables
WELDING TECHNOLOGY
Don't let the questions
Continue to haunt you
Arc instability
Unsightly molding
Excessive spatter
It is suitable for welding 18%Cr-8%Ni stainless steel (SUS304, 304L, etc.) in petrochemical industry,.
Pressure vessel, food machinery, medical machinery, chemical fertilizer and other industries.
Ripple fine
Weld metal contains appropriate amount of ferrite
Crack sensitivity is low, arc is soft and stable, less splash, beautiful forming,
good slag removal, stable wire feeding, with excellent welding process performance.
Easy slagging
Product Parameter
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Other |
GB/T RULES | 0.02 | 0.51 | 1.00 | 0.02 | 0.003 | 9.7 | 19.8 | 0.04 | Cu:0.02 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | Elongation/% | IMAPACT VALUE J/℃ | Heat treatment °C*h | |||||
GB/T RULES | - | 595 | 43 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | 1.6 | |||
Voltage(Volt) | 22-36 | 26-38 | |||
Electricity(Amp) | 120-260 | 200-300 | |||
Speed(mm/min) | 15-20 | 18-25 | |||
Dry stretch length(mm) | 15-25 | 15-25 |
Factory support
The product is suitable for a
wide range of applications
WELDING TECHNOLOGY
Safety injection tank
-
JU2000E jack-up drilling rig
-
37,000 ton general cargo ship
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Other |
GB/T RULES | 0.02 | 0.51 | 1.00 | 0.02 | 0.003 | 9.7 | 19.8 | 0.04 | Cu:0.02 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | Elongation/% | IMAPACT VALUE J/℃ | Heat treatment °C*h | |||||
GB/T RULES | - | 595 | 43 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 1.2 | 1.6 | |||
Voltage(Volt) | 22-36 | 26-38 | |||
Electricity(Amp) | 120-260 | 200-300 | |||
Speed(mm/min) | 15-20 | 18-25 | |||
Dry stretch length(mm) | 15-25 | 15-25 |