Stainless Steels Manual Electrode E309L-15 Carbon steel and stainless steel tower welding
WELDING TECHNOLOGY
Don't let the questions
Continue to haunt you
Arc instability
Unsightly molding
Excessive spatter
It is often used for dissimilar steel
welding of stainless steel and carbon steel.
Or used in poor toughness of martensite, ferritic stainless steel welding.
Ripple fine
Low hydrogen stainless steel hand electrode, the main component is low C-22%Cr-12%Ni, low carbon content and good crack resistance
Good welding operation, stable arc, beautiful forming,
delicate ripple, little splash, easy slag removal;
The coating has good fire resistance, good porosity resistance,
stable mechanical properties of molten metal, and high X-Ray pass rate.
Easy slagging
Product Parameter
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Other |
GB/T RULES | 0.032 | 1.06 | 0.67 | 0.027 | 0.006 | 13.25 | 23.6 | 0.04 | 0.01 | - |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | Heat treatment °C*h | ||||
GB/T RULES | 595 | 38 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Factory support
The product is suitable for a
wide range of applications
WELDING TECHNOLOGY
-
Welding materials for aluminum alloys
-
Three doors 2# is inactive
-
300,000-ton bulk carrier
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Other |
GB/T RULES | 0.032 | 1.06 | 0.67 | 0.027 | 0.006 | 13.25 | 23.6 | 0.04 | 0.01 | - |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | Heat treatment °C*h | ||||
GB/T RULES | 595 | 38 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |