Stainless Steels Manual Electrode E310-15 petrochemical refining and chemical integration electrode
WELDING TECHNOLOGY
Don't let the questions
Continue to haunt you
Arc instability
Unsightly molding
Excessive spatter
Suitable for high temperature resistant products
such as high temperature furnace, coal coking equipment,
can also be used for dissimilar materials welding.
Low hydrogen pure austenitic stainless steel
hand electrode, the main composition is 25%Cr-20%Ni.
Ripple fine
Stable high temperature performance,
can be used up to 1150C environment
Excellent welding performance, excellent fire resistance,
good porosity resistance, stable mechanical properties of molten metal.
Easy slagging
Product Parameter
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Other |
GB/T RULES | 0.102 | 1.66 | 0.4 | 0.27 | 0.005 | 21.8 | 25.6 | 0.06 | 0.10 | - |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | Heat treatment °C*h | ||||
GB/T RULES | 595 | 34 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Factory support
The product is suitable for a
wide range of applications
WELDING TECHNOLOGY
Harbin electric
three gate CMT
-
CJ50
jack-up drill
-
Xinjiang Kela 2 Central
treatment plant project
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | Other |
GB/T RULES | 0.102 | 1.66 | 0.4 | 0.27 | 0.005 | 21.8 | 25.6 | 0.06 | 0.10 | - |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | Heat treatment °C*h | ||||
GB/T RULES | 595 | 34 | - | - |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 30-55 | 50-85 | 80-120 | 100-150 | 140-180 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |