Stainless steels Manual electrode E320-16 weld fabrication stuff
Application
It is suitable for many situations where sulfuric acid, sulfite and their salts are required to resist severe corrosion. It is generally used for welding base materials with similar compositions, such as Alloy20 and UNS N08020, etc. It is widely used in the manufacturing of chemical and hydrogen production equipment
Certification body:JIS
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | else | |
GB/T RULES | 0.07 | 0.5-2.5 | 0.60 | 19.0-21.0 | 32.0-36.0 | 2.0-3.0 | 0.04 | 0.03 | Cu3.0-4.0/Nb+Ta:8*C-1.00 | |
AWS RULES | 0.07 | 0.5-2.5 | 1.00 | 19.0-21.0 | 32.0-36.0 | 2.0-3.0 | 0.04 | 0.03 | Cu3.0-4.0/Nb+Ta:8*C-1.00 | |
EXAMPLE VALUE | 0.016 | 0.74 | 0.8 | 19.7 | 34.3 | 2.8 | 0.011 | 0.002 | Cu3.3/Nb+Ta:0.28 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | ||||
GB/T RULES | - | 550 | - | 28 | ||||
AWS RULES | - | 550 | - | 30 | ||||
EXAMPLE VALUE | - | 575 | 37/-196 | 35 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |
Titanium calcium stainless steel hand electrode, the main composition is 20%Cr-34%Ni-2.5%Mo-3%Cu;
Stable arc, beautiful forming, delicate ripple, little splash, easy slag removal, excellent fire resistance, good porosity resistance, with excellent corrosion and oxidation resistance.
Ningbo Honest Metal Materials Co,Ltd.is an international welding professional company withindependent research and development, production, sales and management. It was established in 2020.
308,000 tons VLCC crude oil carrier
Canada LNG Project
Upper core SG
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | else | |
GB/T RULES | 0.07 | 0.5-2.5 | 0.60 | 19.0-21.0 | 32.0-36.0 | 2.0-3.0 | 0.04 | 0.03 | Cu3.0-4.0/Nb+Ta:8*C-1.00 | |
AWS RULES | 0.07 | 0.5-2.5 | 1.00 | 19.0-21.0 | 32.0-36.0 | 2.0-3.0 | 0.04 | 0.03 | Cu3.0-4.0/Nb+Ta:8*C-1.00 | |
EXAMPLE VALUE | 0.016 | 0.74 | 0.8 | 19.7 | 34.3 | 2.8 | 0.011 | 0.002 | Cu3.3/Nb+Ta:0.28 |
MECHANICAL PROPERTY:
PROPERTY | YIELD STRENGTH(MPa) | EXTENSION STRENGTH(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | ||||
GB/T RULES | - | 550 | - | 28 | ||||
AWS RULES | - | 550 | - | 30 | ||||
EXAMPLE VALUE | - | 575 | 37/-196 | 35 |
RECOMMENDED WELDING PARAMETERS:
DIAMETERS SPECIFICATIONS(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||
ELECTRICITY (Amp) |
H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||
O/W | 20-50 | 45-80 | 70-110 | 90-135 | - |