AWS E307-16 Stainless steels Manual electrode Welding materials

Titanium calcium type stainless steel electrode, alternating and straight, with excellent crack resistance. Used FOR WELDING ASTM307 STEEL AND OTHER DISSIMILAR STEEL, ALSO used for SURfacing OF impact resistant, CORROSION RESISTANT steel and transition layer, such AS HIGH MANGANESE steel, QUENched steel.

Item No：: GES-307( E307-16)

Suit for:: Stainless Steel

Brand:: JINGLEI

Power supply polarity:: DC+/AC

Origin:: China

Size:: 2.0*250/2.6*300/3.2*350/5.0*350

Certificate: ISO3581-A:E(18 9 Mn Mo)R 12/ISO3581-B:ES307-16

Welding position: AWS E7018-A1 Low-alloy steels Metal powder welding wire Welding accessories

Send email to us

Product Detail

Sepcification

Product Tags

Application & Standard

1. Suitable for welding of carbon steel and corresponding strength of boiler, pipeline, vehicle,
building, bridge and other structures, such as Q235.

2. The standard we met: GB/T5117 E4315, AWS, ISO2560-A:E 35 3 B 2 2, ISO 2560-B: E4315A

When welding carbon steel, the strength grade of the steel is typically chosen to match the electrode, taking into account the complex structure, thick plate, stiffness, dynamic load, and poor weldability. Low hydrogen type electrodes are typically chosen for their good plasticity, high impact toughness, and crack resistance. If the welding position requires a particular electrode, such as a bottom electrode, vertical downward electrode, or other special electrode, it must be utilized. The welding efficiency can be increased by using iron powder electrodes.

Features

1. Titanium calcium stainless steel electrode, the main composition is 18% CR-8% Ni-4%Mn;
2. Stable arc, beautiful forming, fine ripples, few splashes, easy de-slagging, good fire resistance of drug skin, good stomatal resistance.
3. Stable mechanical properties, X-ray pass rate is high.

A172 hand electrode is equivalent to the stainless steel hand electrode under AWS E307-16 standard for strong impact wear and transition layer surfacing. Q/1001WSH001-2010 Product Name Hardfacing layer hardness Typical application fields, working conditions and parts Description FW-4101 Welding state 180~200HV cold hardening and 40~45HRC high manganese or dissimilar metal welding. Surfacing repair of tools, punch dies, GRAB or middle wheel and large excavator chassis under high stress under strong impact load.

High Carbon steels Solid wire welding accessories

High Carbon steels Manual electrode welding accessories

Company & Factory

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Cu
GB/T RULES	0.04-0.14	3.30-4.75	1.00	18.0-21.5	9.0-10.7	0.5-1.5	0.040	0.03	0.75
AWS RULES	0.04-1.14	3.30-4.75	1.00	18.0-21.5	9.0-10.7	0.5-1.5	0.040	0.03	0.75
EXAMPLE VALUE	0.076	3.65	0.65	19.5	9.8	0.7	0.027	0.003	0.1

MECHANICAL PROPERTY:

PROPERTY	YIELD STRENGTH(MPa)	EXTENSION STRENGTH(MPa)	HEATTREAMENT℃xh	IMAPACT VALUE J/℃	ELONGATION(%)
GB/T RULES	-	590	-	-	25
AWS RULES	-	590	-	-	30
EXAMPLE VALUE	-	610	-	-	38

RECOMMENDED WELDING PARAMETERS:

DIAMETERS SPECIFICATIONS(mm)		2.0*250	2.6*300	3.2*350	4.0*350	5.0*350
ELECTRICITY (Amp)	H/W	50-75	70-95	80-120	110-160	160-190
	O/W	20-50	45-80	70-110	90-135	-

PACKING DETAILES：

SEPCIFICATION	LENGTH	PCS/1KG	WEIGHT/1KG
2.0mm	300mm	79PCS	2KG
2.6mm	300mm	48PCS	2KG
3.2mm	350mm	27PCS	5KG
4.0mm	350mm	16PCS	5KG
5.0mm	350mm	12PCS	5KG

NOTE:
H/W: horizontal position welding
O/W: over-head position welding

TYPICAL CASES

430Mpa Hand Electrode For Low Carbon Steel05

Certificates

Product composition and mechanical properties introduction

CHEMICAL COMPONET:

ALLOY(wt%)	C	Mn	Si	Cr	Ni	Mo	P	S	Cu
GB/T RULES	0.04-0.14	3.30-4.75	1.00	18.0-21.5	9.0-10.7	0.5-1.5	0.040	0.03	0.75
AWS RULES	0.04-1.14	3.30-4.75	1.00	18.0-21.5	9.0-10.7	0.5-1.5	0.040	0.03	0.75
EXAMPLE VALUE	0.076	3.65	0.65	19.5	9.8	0.7	0.027	0.003	0.1

MECHANICAL PROPERTY:

PROPERTY	YIELD STRENGTH(MPa)	EXTENSION STRENGTH(MPa)	HEATTREAMENT℃xh	IMAPACT VALUE J/℃	ELONGATION(%)
GB/T RULES	-	590	-	-	25
AWS RULES	-	590	-	-	30
EXAMPLE VALUE	-	610	-	-	38